YIN Bang-yue, WANG Ling-sen(China Institute of Atomic Energy, P.O. Box 275-51, Beijing 102413, China;State Key Laboratory for Powder Metallurgy, Central South University, Changsha 410083, China). Study on Mechanical Strength of the Hot-pressed Sintered Boron Carbide Ceramic[J]. Atomic Energy Science and Technology, 2004, 38(6): 522-522. DOI: 10.7538/yzk.2004.38.06.0522
Citation: YIN Bang-yue, WANG Ling-sen(China Institute of Atomic Energy, P.O. Box 275-51, Beijing 102413, China;State Key Laboratory for Powder Metallurgy, Central South University, Changsha 410083, China). Study on Mechanical Strength of the Hot-pressed Sintered Boron Carbide Ceramic[J]. Atomic Energy Science and Technology, 2004, 38(6): 522-522. DOI: 10.7538/yzk.2004.38.06.0522
shu
    Graphical Abstract
    • Abstract
  • The room and high temperature mechanical strength of the hot-pressed B4C ceramic are studied. The results show that the hot-pressed B4C ceramic sintered at 2 150℃for 10 minutes from the jet-milled powders(3. 85μm), has the density of 91. 6%T. D. (T. D.--theoretic density), and the room temperature bending strength andcompression strength are 280 and 1 463 MPa, respectively. However, the hot-pressed B4C ceramic from the vibratory-milled powders(0. 35 μm) has a relative density of 99. 7% T. D., and the room temperature bending strength and compression strength are 515 and 2 870 MPa, respectively. The bending strengths of both ceramics decrease slowly with increasing temperatures, but the compression strengths decrease quickly below 600℃ and decrease slowly above 600℃. At last, the relationship between mechanical strength of both B4C ceramics and temperature and porosity is discussed by use of the empirical formulae.
    • FullText(HTML)
  • loading
    • References (7)
    • Related Articles

Catalog

    Turn off MathJax
    Article Contents

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return